Resin Technical Parameters
Solidify Wavelength: 405nm
Bending Modulus: 1.882-2.385 Gpa
Bending Strength: 59-70 MPa
Hot Deformation Temperature: 80 ℃(176°F)
Volume Shrinkage: 3.72-4.24%
Tensile Strength: 36-52 MPa
Tensile Modulus: 1.779-2.385 GPa
Elongation at Break: 11% -20%
Shore Hardness: 84D
Glass Transition Temperature: 100 ℃(212°F)
Density: 1.05-1.25 g/cm3
Notched Izod Impact Strength:44-49 j/m
Shelf Life: 1 year
Bottom exposure time(s): 30-60 s/layer
Normal exposure time: 6-10 s/layer
Note: The material’s actual properties depend on the printing process conditions, the design structure and its purpose, test conditions, etc.
-Shake the bottle before pouring the resin into the tank.
-Wear gloves and masks before using to avoid direct skin contact.
-Avoid printing too many items at the same time. Divide your production into several stages to achieve better results.
-Clean finished models with IPA or Ethanol. Dip in alcohol bath and/or clean with soft brush remaining resin on the model.
-Recommended storage temperature 20 °C – 30 °C.
-To preserve the resin’s characteristics, filter the liquid after each printing process and protect the containers from direct sunlight.
Make sure this fits by entering your model number.
[Great Stability] SHINE SING UV curing resin is specially designed to shorten the curing time with its excellent fluidity, and ensures a smooth and stable printing experience.
[High Precision Details and Toughness] The 3D printed objects came out pretty hard with high accuracy and good detail. Also finished models are easy to clean well with IPA or Ethanol.
[Wide Compatibility] Compatible for most wavelength 405nm LCD/DLP resin 3D printers, apply for dental design, Garage Kits etc.
[Bright and Available Colors] SHINE SING 3D printer rapid resin is manufactured with high-quality pigments and photoinitiators, make the printed models show bright and stunning color effect.
[Safe and Reliable] The resin passed MSDS certification. Leak-proof bottle and completely wrapped in a bubble bag, make the photopolymer resin intact during transportation.